Fabrication of the Ni3Al - Zr materials by mechanical activation and spark plasma sintering

Fabrication of the Ni3Al - Zr materials by mechanical activation and spark plasma sintering Научная публикация

Конференция

INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS WITH HIERARCHICAL STRUCTURE FOR NEW TECHNOLOGIES AND RELIABLE STRUCTURES 2019
01-05 окт. 2019 , Томск

Журнал

AIP Conference Proceedings
ISSN: 0094-243X

Вых. Данные

Год: 2019, Том: 2167, Номер статьи : 020328, Страниц : 5 DOI: 10.1063/1.5132195

Авторы

Shevtsova L.I. ¹ , Nemolochnov D.A. ¹ , Esikov M.A. ^1,2 , Gavrilov A.I. ³ , Lozhkina E.A. ¹ , Cherkasova N.Yu. ¹ , Malikov V.N. ⁴

Организации

1	Novosibirsk State Technical University
2	Lavrentyev Institute of Hydrodynamics SB RAS
3	Institute of Solid State Chemistry and Mechanochemistry SB RAS
4	Altay State University

The investigation of the structure and mechanical properties of the intermetallic Ni3Al fabricated by spark plasma sintering of mechanically activated Ni and Al powders with zirconium addition in an amount of 0.1 and 1 wt.% are conducted. A single Ni3Al phase is formed in the compacts with milled powders and with different zirconium content. Relative density of all sintered samples is ~97 %. Microhardness of the sintered Ni3Al is 6.1 GPa. Microhardness of the sintered Ni3Al with zirconium addition is ~6.5 GPa. The results show that spark plasma sintering at 1100°C of the powder mixture Ni3Al with zirconium addition in an amount of 1 wt.% after mechanical alloying for three minutes leads to the formation of material with the value of bending strength equal to 930 MPa.

Shevtsova L.I. , Nemolochnov D.A. , Esikov M.A. , Gavrilov A.I. , Lozhkina E.A. , Cherkasova N.Y. , Malikov V.N.
Fabrication of the Ni3Al - Zr materials by mechanical activation and spark plasma sintering
AIP Conference Proceedings. 2019. V.2167. 020328 :1-5. DOI: 10.1063/1.5132195 Scopus РИНЦ OpenAlex

Scopus:	2-s2.0-85075800701
РИНЦ:	43214263
OpenAlex:	W2990058890

БД	Цитирований
Scopus	2
OpenAlex	2
РИНЦ	1