Influence of O2/C2H2 ratio on microstructure and functional properties of Fe-based detonation-sprayed coatings with an amorphous phase

Influence of O2/C2H2 ratio on microstructure and functional properties of Fe-based detonation-sprayed coatings with an amorphous phase Научная публикация

Журнал

Surface and Coatings Technology
ISSN: 0257-8972

Вых. Данные

Год: 2026, Номер статьи : 133637, Страниц : 14 DOI: 10.1016/j.surfcoat.2026.133637

Ключевые слова

Detonation spraying, Coating, Amorphous phase, Oxygen-to-fuel ratio, Wear resistance, Corrosion resistance

Авторы

Wang Xichuan ¹ , Kuchumova Ivanna D. ² , Batraev Igor S. ² , Ulianitsky Vladimir Yu. ² , Lu Wenfei ¹ , Shen Jun ¹

Организации

1	Fujian University of Technology, School of Materials Science and Engineering, Fuzhou, 350118, China
2	Lavrentyev Institute of Hydrodynamics SB RAS, 15, Lavrentyev Ave., Novosibirsk, 630090, Russia

This study presents the results of an investigation into the influence of the oxidiser/fuel (O/F) ratio of an oxygenacetylene (O2 + C2H2) explosive gas mixture on the phase composition, microstructure, wear resistance, and electrochemical behaviour of Fe49.7Cr18Mn1.9Mo7.4W1.6B15.2C3.8Si2.4 coatings fabricated by detonation spraying. The obtained results demonstrate that the O/F ratio plays an important role in regulating coating densification and structural integrity. Due to the high velocity and temperature of the powder particles during the spraying process, as well as the low content of oxygen-containing elements in the detonation products, the coating obtained at O/F = 1.1 from the powder with a predominantly crystalline structure had the highest content of the amorphous phase (80 vol%). Close values of porosity (~2%) of the coatings deposited at O/F ratio of 1.1–1.3 resulted in similarly wear and corrosion resistance. This demonstrates the importance of developing multifunctional coatings made from amorphous alloys with not only a low crystalline phase content, but also a low porosity. The obtained results establish a clear relationship between “process–microstructure–properties”, providing practical recommendations for determining the processing window for production of high-quality Febased amorphous coatings by detonation spraying.

Wang X. , Kuchumova I.D. , Batraev I.S. , Ulianitsky V.Y. , Lu W. , Shen J.
Influence of O2/C2H2 ratio on microstructure and functional properties of Fe-based detonation-sprayed coatings with an amorphous phase
Surface and Coatings Technology. 2026. 133637 :1-14. DOI: 10.1016/j.surfcoat.2026.133637 OpenAlex

Поступила в редакцию:	24 февр. 2026 г.
Принята к публикации:	26 мая 2026 г.
Опубликована online:	28 мая 2026 г.