Microstructure, mechanical and tribological properties of cold sprayed Cu[sbnd]W coatings Научная публикация

Журнал International Journal of Refractory Metals and Hard Materials
ISSN: 0263-4368
Вых. Данные Год: 2022, Том: 106, Номер статьи : 105866, Страниц : 9 DOI: 10.1016/j.ijrmhm.2022.105866
Ключевые слова Cold spray; Composite; Copper‑tungsten; Dry sliding wear; Mechanical properties; Microstructure
Авторы Shikalov Vladislav S. 1 , Vidyuk Tomila M. 1 , Filippov Artem A. 1 , Kuchumova Ivanna D. 2
Организации
1 Khristianovich Institute of Theoretical and Applied Mechanics SB RAS, Institutskaya str. 4/1, Novosibirsk 630090, Russia
2 Lavrentyev Institute of Hydrodynamics SB RAS, Lavrentyev Ave. 15, Novosibirsk 630090, Russia

Информация о финансировании (1)

1 Министерство науки и высшего образования Российской Федерации FWGG-2022-0001

Реферат: This paper presents the results of the investigation of the microstructure and properties of copper‑tungsten coatings with different compositions on aluminum alloy substrates. Coatings were obtained by cold spray method using powder mixtures as feedstock. The effect of the powder mixture composition on the deposition efficiency and the tungsten content in the coating have been studied. X-ray diffraction analysis was used to investigate the phase composition and to reveal the peculiarities of changes in the crystalline structure of copper and tungsten particles after cold spraying in relation to the coating composition. Using the method of instrumental indentation on cross-sections of the coatings mechanical properties were measured. It was shown that increasing of tungsten content in the coatings contributes to increasing the microhardness and Young's modulus of the coatings. The mapping images showed that all coatings were characterized by non-uniformity of mechanical properties over the cross-section. The bonding strength of coatings significantly increases with increasing tungsten content in the feedstock. Cu[sbnd]W coatings are characterized by lower specific wear rate values and higher coefficients of friction under dry sliding wear conditions in a ball-on-flat mode compared to pure copper coating.
Библиографическая ссылка: Shikalov V.S. , Vidyuk T.M. , Filippov A.A. , Kuchumova I.D.
Microstructure, mechanical and tribological properties of cold sprayed Cu[sbnd]W coatings
International Journal of Refractory Metals and Hard Materials. 2022. V.106. 105866 :1-9. DOI: 10.1016/j.ijrmhm.2022.105866 WOS Scopus РИНЦ OpenAlex
Идентификаторы БД:
Web of science: WOS:000800537900002
Scopus: 2-s2.0-85129014666
РИНЦ: 48433472
OpenAlex: W4224885887
Цитирование в БД:
БД Цитирований
Scopus 15
OpenAlex 16
РИНЦ 12
Web of science 13
Альметрики: