Morphological features and phase composition of W-containing coatings formed on diamond via its interaction with WO3 Научная публикация

Журнал Diamond and Related Materials
ISSN: 0925-9635
Вых. Данные Год: 2022, Том: 123, Страницы: 108876 Страниц : 1 DOI: 10.1016/j.diamond.2022.108876
Ключевые слова Diamond; Scanning electron microscopy; Selective deposition; W-containing coatings
Авторы Ukhina A.V. 1 , Dudina D.V. 1,2,3 , Bokhonov B.B. 1 , Savintseva D.V. 3 , Samoshkin D.A. 4 , Stankus S.V. 4
Организации
1 Institute of Solid State Chemistry and Mechanochemistry, Siberian Branch of the Russian Academy of Sciences
2 Lavrentyev Institute of Hydrodynamics, Siberian Branch of the Russian Academy of Sciences
3 Novosibirsk State Technical University,
4 Kutateladze Institute of Thermophysics, Siberian Branch of the Russian Academy of Sciences

Информация о финансировании (1)

1 Министерство науки и высшего образования Российской Федерации FWGG-2021-0005

Реферат: In the present work, W-containing coatings were deposited on the surface of diamond microcrystals. The coatings formed as diamond reacted with a WO3 powder in the die of a hot press at elevated temperatures. The morphology and phase composition of the coatings were studied as functions of the treatment temperature and treatment time. The coated diamond crystals were investigated by X-ray diffraction, scanning electron microscopy, and energy-dispersive spectroscopy. After treatment of the mixture at 850 °C for 15 min, WO2 and W18O49 were found on the diamond surface. After treatment at 950 °C (15 min), tungsten was the dominant phase of the coating. Treatment at 1150 °C (15 min) led to the formation of the WC and W2C phases; no metallic tungsten was present in the coating obtained at this temperature. The reaction sequence describing the coating formation process was proposed. During the coating formation, the deposition selectivity with regard to the diamond facet was observed. The {100} facets of diamond were preferentially coated. The coating developed through the formation and coalescence of islands, which were of square shape on the {100} facets and of triangular shape on the {111} facets of diamond.
Библиографическая ссылка: Ukhina A.V. , Dudina D.V. , Bokhonov B.B. , Savintseva D.V. , Samoshkin D.A. , Stankus S.V.
Morphological features and phase composition of W-containing coatings formed on diamond via its interaction with WO3
Diamond and Related Materials. 2022. V.123. P.108876. DOI: 10.1016/j.diamond.2022.108876 WOS Scopus РИНЦ OpenAlex
Идентификаторы БД:
Web of science: WOS:000787889900007
Scopus: 2-s2.0-85123891183
РИНЦ: 48146853
OpenAlex: W4210489112
Цитирование в БД:
БД Цитирований
Scopus 4
OpenAlex 5
РИНЦ 5
Web of science 4
Альметрики: