Structural-Phase Evolution during In Situ Mechanochemical Synthesis of Titanium Carbide in a Nickel Matrix

Structural-Phase Evolution during In Situ Mechanochemical Synthesis of Titanium Carbide in a Nickel Matrix Научная публикация

Журнал

Physics of Metals and Metallography
ISSN: 0031-918X

Вых. Данные

Год: 2024, Том: 125, Номер: 10, Страницы: 1166-1173 Страниц : 8 DOI: 10.1134/S0031918X24601240

Ключевые слова

mechanochemical synthesis, mechanically stimulated reaction, composites, nickel, titanium carbide

Авторы

Grigoreva T.F. ¹ , Dudina D.V. ^1,2 , Vidyuk T.M. ^1,3 , Kovaleva S.A. ⁴ , Ukhina A.V. ¹ , Devyatkina E.T. ¹ , Vosmerikov S.V. ¹ , Lyakhov N.Z. ¹

Организации

1	Institute of Solid State Chemistry and Mechanochemistry SB RAS
2	Lavrentiev Institute of Hydrodynamics SB RAS
3	Khristianovich Institute of Theoretical and Applied Mechanics SB RAS
4	Joint Institute of Mechanical Engineering NASB, Minsk

Информация о финансировании (1)

Министерство науки и высшего образования Российской Федерации

FWGG-2021-0005

The structural and phase evolution of powders in a Ni–Ti–C ternary system with 50 wt % Ni during mechanochemical synthesis in an AGO-2 planetary ball mill was studied using X-ray diffraction analysis and scanning electron microscopy. The formation of titanium carbide in the presence of nickel was found to be accelerated, and proceeds in a mechanically stimulated reaction mode with an induction period of less than two minutes. The value of the nickel lattice parameter was observed to increase up to 0.35733 nm with increasing mechanical activation time. The products of mechanochemical synthesis, subjected to four minutes of mechanical activation, are titanium carbide, a solid solution of titanium and carbon in nickel, and iron (approximately 1 wt %, resulting from milling) with agglomerate sizes of 1–30 μm.

Grigoreva T.F. , Dudina D.V. , Vidyuk T.M. , Kovaleva S.A. , Ukhina A.V. , Devyatkina E.T. , Vosmerikov S.V. , Lyakhov N.Z.
Structural-Phase Evolution during In Situ Mechanochemical Synthesis of Titanium Carbide in a Nickel Matrix
Physics of Metals and Metallography. 2024. V.125. N10. P.1166-1173. DOI: 10.1134/S0031918X24601240 WOS Scopus РИНЦ OpenAlex

Web of science:	WOS:001381827400001
Scopus:	2-s2.0-85212770601
РИНЦ:	75154890
OpenAlex:	W4405658087

Пока нет цитирований