Formation of metastable phases during spark plasma sintering of Fe@Au core–shell particles Научная публикация

Журнал Philosophical Magazine
ISSN: 1478-6435
Вых. Данные Год: 2024, Страницы: 1-17 Страниц : 17 DOI: 10.1080/14786435.2024.2352015
Авторы Bokhonov Boris B. 1 , Sharafutdinov Marat R. 1 , Dudina Dina V. 1,2
Организации
1 Institute of Solid State Chemistry and Mechanochemistry of SB RAS
2 Lavrentyev Institute of Hydrodynamics

Информация о финансировании (1)

1 Министерство науки и высшего образования Российской Федерации FWGG-2021-0005

Реферат: The present work reports the formation of Fe-Au metastable alloys by galvanic replacement, pressureless spark plasma sintering (SPS) and acid treatment. The reaction of partial galvanic replacement between micrometer-sized iron particles and HAuCl4 solution allowed synthesising core–shell Fe@Au particles. When the Fe@Au particles were treated in HCl solution, iron was selectively dissolved and hollow Au particles were formed. Pressureless SPS of the Fe@Au core–shell particles led to the formation of a metastable intermetallic phase, FeAu3, and a supersaturated solid solution, Au(Fe). The latter was resistant to HCl solution; at the same time, the FeAu3 phase decomposed during HCl treatment to form a porous gold structure. This work shows that a combination of galvanic replacement, SPS and acid treatment can be used for the preparation of metastable Fe-Au alloys with different phase compositions and particle morphologies.
Библиографическая ссылка: Bokhonov B.B. , Sharafutdinov M.R. , Dudina D.V.
Formation of metastable phases during spark plasma sintering of Fe@Au core–shell particles
Philosophical Magazine. 2024. P.1-17. DOI: 10.1080/14786435.2024.2352015 WOS Scopus РИНЦ OpenAlex
Даты:
Поступила в редакцию: 26 февр. 2024 г.
Опубликована online: 15 мая 2024 г.
Идентификаторы БД:
Web of science: WOS:001223877300001
Scopus: 2-s2.0-85193064738
РИНЦ: 67874029
OpenAlex: W4396925508
Цитирование в БД:
БД Цитирований
OpenAlex 2
Scopus 2
Web of science 2
Альметрики: