Реферат: This paper describes an experimental study of a temperature effect on the fracture of laser welded joints of Mg- and Cu-containing aviation aluminum alloys. The fracture of alloys and their welded joints under a uniaxial loading at temperatures of −60, 20, and 85◦C is under study. It is revealed that the strength and ultimate strain of welded joints of Cu-containing alloys decrease as temperature rises because of the formation of fixed zones of localized plastic shears. Heating and cooling suppress the Portevin–Le Chatelier effect and significantly reduce the ultimate strain of a Mg-containing alloy, even though such reduction is not observed in a welded joint. It is shown that, the maximum limiting elongation of the welded joint of a Mg-containing alloy is achieved at a negative temperature, while the formation of secondary cracks is begins during heating.

Библиографическая ссылка: Karpov E.V. , Malikov A.G. , Orishich A.M. , Annin B.D.
Temperature Effect on the Fracture of Laser Welded Joints of Aviation Aluminum Alloys
Journal of Applied Mechanics and Technical Physics. 2018. V.59. N5. P.934-940. DOI: 10.1134/s002189441805022x WOS Scopus РИНЦ OpenAlex

Оригинальная: Карпов Е.В. , Маликов А.Г. , Оришич А.М. , Аннин Б.Д.
Влияние температуры на разрушение лазерных сварных соединений алюминиевых сплавов авиационного назначения
Прикладная механика и техническая физика. 2018. Т.59. №4. С.191-199. DOI: 10.15372/pmtf20180522 РИНЦ OpenAlex

Идентификаторы БД:

Web of science:	WOS:000455182800022
Scopus:	2-s2.0-85056230093
РИНЦ:	38206043
OpenAlex:	W2900256552

Цитирование в БД:

БД	Цитирований
Scopus	5
OpenAlex	7
РИНЦ	5
Web of science	4

Альметрики: